CUARSIL IS4-1 AC BIG-BAG 1500 CONICOS

CHECK IN AND CONSULT THE PRICE

Availability: In stock

Characteristics:


Dry silica mass based on high purity microcrystalline quartzite, mixed with Boric Acid (H3BO3) -AC as a sintering agent.


It may also be delivered without any sintering agent.


Application:


Lining of high, medium and low frequency coreless induction furnaces.


High temperature melting .


Grey or nodular iron, heavy non-ferrous metals and steel casting.

CUARSIL  IS4-1  AC BIG-BAG 1500 CONICOS

Double click on above image to view full picture

Zoom Out
Zoom In

More Views

CHECK IN AND CONSULT THE PRICE

Insertec Technical Data Sheet

Humidity xx
Caracteristicas Dry silica mass based on high purity microcrystalline quartzite, mixed with Boric Acid (H3BO3) -AC as a sintering agent. It may also be delivered without any sintering agent.
Application Lining of high, medium and low frequency coreless induction furnaces high temperature melting grey or nodular iron, heavy non-ferrous metals and steel casting.
Temperature Depends on binding percentage. It varies between 1,400ºC (for 2.2% Boric Acid and 1.2% Boron Oxide) and 1,650ºC (for 1% Boric Acid and 0.5% Boron Oxide).
Grain Size Distribution 0 – 4 mm
Tipo de Ligante Acido Bórico (H3B03) entre 1 y 2,5%, para IS4 – AC Son valores medios que pueden variar en +10 % del porcentaje de ligante
Chemical Analysis Al2O3 max. 0.9 % SiO2 98 – 99 % Fe2O3 max. 0.4 %
Density > 2,080 Kg/m3
Installation Por apisonado en seco manualmente o con equipos de vibrado específicos para fondo y paredes. Véase Cuaderno de instrucciones.
Storage Los pallets deben almacenarse en sitio seco, una vez abierto un pallet debe consumirse totalmente o los sacos sobrantes se cubrirán con plástico. Duración máxima: 12 meses.
Packing Sacos de papel de 25 kg. PALLET 1000kg
Drying and Heating Calentar hasta la temperatura de trabajo a razón de 100-180ºC/h. (para ligante óxido bórico) o 60-120ºC/h. (para ácido bórico) en función de la capacidad del horno. El sinterizado se realizará a 30-50ºC por encima de la temperatura de trabajo, manteniendo